The following tables provide a list of Brinell hardness (HB) values for common aluminum alloys. All values are taken at room temperature (approximay 20°C or 68°F). The
Aluminum 6061-T6 is the one of the most common types of aluminum metals used in the industrial world today. With its high strength-to-weight ratio and excellent mability, it
Property 6061-T4 6061-T6 Density 2.70 g/cc | 0.0975 lb/in³ 2.70 g/cc | 0.0975 lb/in³ Mechanical Properties Property 6061-T4 6061-T6 Tensile Strength 241 MPa | 35000 psi
Specific Heat Capacity. 900 J/kg-K 0.21 BTU/lb-°F. Thermal Conductivity. 170 W/m-K 97
the Hardness of Aluminum 6061 Alloy during Microarc Oxidation process L. Shehadeh1, K. Mohamed1, U. Al- Qawabeha2, B. Abu Jadayel3 United Arab Emirates Abstract - Aluminum 6061 alloy is the most frequently used aluminum alloy in automobile, aircraft, and aerospace industries. However, poor wear and corrosion resistances,
6061-T6 aluminum belongs to the aluminum alloys classification, while AISI 304 stainless steel belongs to the iron alloys. There are 32 material properties with values for both materials. Brinell Hardness: 93: 170 to 360: Elastic (Young\'s, Tensile) Modulus, GPa: 69: 200: Elongation at Break, % 10: 8.0 to 43: Fatigue Strength, MPa:
6061-T62 aluminum is 6061 aluminum in the T62 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. Brinell Hardness. 88. Elastic (Young\'s, Tensile) Modulus. 69 GPa 10 x psi. Elongation at Break. 8.7 % Fatigue Strength. 100 MPa
UNS A96061; ISO AlMg1SiCu; Aluminium 6061-T651, AD-33 (Russia); AA6061-T651 Physical Properties Metric English Comments Density 2.70 g/cc 0.0975 lb/in³ AA; Typical Mechanical Properties Metric English Comments Hardness, Brinell AA; Typical; 500 g load; 10 mm ball Hardness, Knoop Converted from Brinell Hardness Value
Aluminum 6061-T4; 6061-T451. Subcategory: 6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal. Close Analogs: Hardness, Knoop: 88: 88 Converted from Brinell Hardness Value: Hardness, Vickers: 75: 75 Converted from Brinell Hardness Value: Ultimate Tensile Strength: 241 MPa: 35000
Hardness, Rockwell B : 60: 60: Converted from Brinell Hardness Value: Hardness, Vickers: 107: 107: Converted from Brinell Hardness Value: Ultimate Tensile Strength: 310 MPa: 45000 psi: Aluminum 6061-T6 is the one of the most common types of aluminum metals used in the industrial world today. With its high strength-to-weight ratio and
Aluminum alloys are generally softer than other metals, such as steel or titanium. However, the hardness of aluminum alloys can vary widely depending on the alloying elements present and the heat treatment process used. The following tables provide a list of Brinell hardness (HB) values for common aluminum
al6061-T651, UNS A96061; ISO AlMg1SiCu; Aluminium 6061-T6, AD-33 (Russia); AA6061-T6; 6061T6, ISO AlMg1SiCu; Aluminium 6061-T651, AD-33 (Russia); AA6061-T651, General 6061 characteristics and uses: Excellent joining characteristics, good acceptance Hardness, Knoop, Converted from Brinell Hardness Value; Hardness, Rockwell A,
6061-T6 aluminum is 6061 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. Brinell Hardness. 93. Elastic (Young\'s, Tensile) Modulus. 69 GPa 10 x psi. Elongation at Break. 10 % Fatigue Strength. 96 MPa 14
As can be seen from Fig. 9, the hardness of 6061 aluminum alloy is 73.9 HV under air cooling mode, the hardness of 6061 aluminum alloy is .7 HV under water cooling mode, and the hardness of 6061 aluminum alloy is 69.7 HV under furnace cooling mode, in which the difference between the maximum hardness value and the minimum
Hardness, Knoop Hardness, Vickers Ultimate Tensile Strength Tensile Yield Strength ALUMINUM COMMON GRADE 6061 WITH T4Aluminum Alloy Common Grade 6061 w/T4 Temper Alliance LLC 1150 Eastport Center Dr. Valparaiso, IN. 46383 : 219-548-3799 :
Lastly, 6061 aluminum does not work as much as 5052 aluminum making it unsuitable for certain applications requiring a higher hardness. Overall, 6061 aluminum is an excellent all-purpose alloy that offers good strength and formability at an economical
6061-T6 aluminum belongs to the aluminum alloys classification, while SAE-AISI 1018 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Brinell Hardness: 93: 130 to 140: Elastic (Young\'s, Tensile) Modulus, GPa: 69: 190: Elongation at Break, % 10: 17 to 27: Fatigue Strength, MPa: 96: 180 to
Hardness: The hardness of 6061-T6 aluminum is usually tested on the Brinell scale, which shows that it has a moderate amount of hardness. This quality makes it easier to work with and harder to wear down. – Elasticity: Because 6061-T6 aluminum has a good elastic elasticity, it can withstand pressure without permanently changing